Liquid metal embrittlement (also known as LME and liquid metal induced embrittlement) is a phenomenon of practical importance, where certain ductile metals experience drastic loss in tensile ductility or undergo brittle fracture when exposed to specific liquid metals. Generally, tensile stress, either externally applied or internally present, is needed to induce embrittlement. Exceptions to this rule have been observed, as in the case of aluminium in the presence of liquid gallium.[1] This phenomenon has been studied since the beginning of the 20th century. Many of its phenomenological characteristics are known and several mechanisms have been proposed to explain it.[2][3] The practical significance of liquid metal embrittlement is revealed by the observation that several steels experience ductility losses and cracking during hot-dip galvanizing or during subsequent fabrication.[4] Cracking can occur catastrophically and very high crack growth rates have been measured.[5]
Similar metal embrittlement effects can be observed even in the solid state, when one of the metals is brought close to its melting point; e.g. cadmium-coated parts operating at high temperature. This phenomenon is known as solid metal embrittlement.[6]
^Huntington, A. K. (1914). "Discussion on Report to Beilby Prize Committee". Journal of the Institute of Metals. 11 (1). London, UK: Institute of Metals: 108.
^Joseph, B.; Picat, M. & Barbier, F. (1999). "Liquid metal embrittlement: A state-of-the-art appraisal". European Physical Journal Applied Physics. 5 (1): 19–31. Bibcode:1999EPJAP...5...19J. doi:10.1051/epjap:1999108.
^Kolman, D. G. (2003). "Environmentally Induced Cracking, Liquid Metal Embrittlement". In Cramer, Stephen D. & Covino, Bernard S. Jr. (eds.). ASM Handbook, Volume 13A, Corrosion: Fundamentals, Testing and Protection. Materials Park, OH: ASM International. pp. 381–392. ISBN 978-0-87170-705-5.
^Kamdar, M. H. (1983). "Liquid Metal Embrittlement". Treatise on Materials Science and Technology. Vol. 25. Academic Press. pp. 361–459.
^Kolman, D.G. & Chavarria, R. (2002). "Liquid-Metal Embrittlement of 7075 Aluminum and 4340 Steel Compact Tension Specimens by Gallium". Journal of Testing and Evaluation. 30 (5): 452–456. doi:10.1520/JTE12336J.
^Kolman, D.G. (2003), pp. 393-397.
and 21 Related for: Liquid metal embrittlement information
Liquidmetalembrittlement (also known as LME and liquidmetal induced embrittlement) is a phenomenon of practical importance, where certain ductile metals...
embrittlement caused by absorption of hydrogen sulfide. Adsorption embrittlement is the embrittlement caused by wetting. Liquidmetalembrittlement (LME)...
Hydrogen embrittlement (HE), also known as hydrogen-assisted cracking or hydrogen-induced cracking (HIC), is a reduction in the ductility of a metal due to...
displaying short descriptions with no spaces Hydrogen embrittlement – Reduction in ductility of a metal exposed to hydrogen Kelvin probe force microscope –...
hydrogen embrittlement due to hydrogen sulfide Notes "Chapter 32: Failure Analysis". Metals Handbook (Desk ed.). American Society for Metals. Gu, B.;...
embrittlement, liquidmetalembrittlement and corrosion fatigue all coming under this category. Environments such as moist air, sea water and corrosive liquids and...
steel, causing extreme loss of strength and ductility called liquidmetalembrittlement. The melting point of gallium, at 302.9146 K (29.7646 °C, 85.5763 °F)...
process may occur by contact with other metals, nonmetallic solids, flowing liquids, solid particles or liquid droplets entrained in flowing gasses. The...
because of solubility changes induced by other factors, e.g., liquid flashing, liquid degassing, redox potential changes, or mixing of incompatible fluid...
transition metals are usually insensitive to temperature. High-strength BCC steels display a wider variation of impact energy than high-strength metal that...
Havilland Comet C1 jet airliners crashed due to decompression caused by metal fatigue, and in 1963–64, when the vertical stabilizer on four Boeing B-52...
hardware, galinstan is electrically conductive and causes liquidmetalembrittlement in many metals including aluminum which is commonly used in heatsinks...
pedestal, which is made of stone, or appearing to be so. A small wooden or metal support is typically called a post. Supports with a rectangular or other...
ecosystem Late Middle English Liquidmetalembrittlement, of solid metals in the presence of some liquidmetals London Metal Exchange, futures exchange,...
The highest specific impulse chemical rockets use liquid propellants (liquid-propellant rockets). They can consist of a single chemical (a monopropellant)...
{\textstyle \mathrm {K} _{\mathrm {c} }} values that are ~5% of that found in metals. However, as demonstrated by Faber and Evans, fracture toughness can be...